Abstract:
Herein, the (Zn0.97−xLixMn0.03)O ( x = 0, 0.01, 0.03, and 0.05 ) thin flms were prepared on a glass substrate via the sol–gel spin coating technique to study the
infuence of lithium on Mn-doped ZnO thin flms for structural, optical, electrical, morphological, chemical, and NO2 gas-sensing applications. According to
the XRD analysis, all samples display a hexagonal wurtite crystal structure. A
FESEM analysis revealed that the incorporation of lithium into Mn-doped ZnO
results in a smaller grain size with more voids than Mn-doped ZnO. Four-probe
Hall measurements revealed the n-type conductivity on (Zn0.97−xLixMn0.03)O
( x = 0 and 0.01), whereas samples with ( x = 0.03 and 0.05 ) exhibited p-type conductivity, which was well explained. XPS and PL spectra confrmed the abundance of surface oxygen vacancies on the prepared sample. It is revealed that
interaction between the defect states of lithium and manganese with inherent
defect states of ZnO play a crucial role in carrier transfer for the gas-sensing process. In contrast to Mn-doped ZnO, (Zn0.96Li0.01Mn0.03)O exhibits smaller grains
and a ninefold gas sensitivity (62.01) toward 75 ppm of NO2 gas at 210 °C toward
75 ppm of NO2 gas with a rapid response (30 s) and recovery (125 s) time